If you run fill without cooling the boundary condition for fill is a uniform mold surface temperature. But if you have chunky parts with bad cooling situation you will miss that in simulation.

So it is better to run a cooling before filling. Than you have a temperature distribution of the mold that is the boundary condition for the filling simulation. This is much more precise.

Philipp